H2SO4 corrosion of API5L-X52 pipeline steel: Thermal

Por favor, use este identificador para citar o enlazar este ítem: http://repositoriodigital.ipn.mx/handle/123456789/10834

Título :	H2SO4 corrosion of API5L-X52 pipeline steel: Thermal
Palabras clave :	Steel corrosion Thermal difusivity
Fecha de publicación :	16-ene-2013
Editorial :	Journal de Physique IV France
Descripción :	The effect of corrosion by H2SO4 on the values of room temperature thermal diffusivity (α) and the microstructure of API5L-X52 pipeline steel are studied. The samples were exposed for 3, 6, 9, 12 and 15 days in a corrosive solution in an atmosphere with relative humidity of 57.16% in average and at temperature of 23.6 °C. The α values were measured by the photoacoustic technique in a heat transmission configuration. Our results show a decrease with the corrosion time (t), with a behavior described by an exponentially decreasing curve. Microestructural study on the samples revealed the appearance of irregular surfaces with corroded grain frontiers, porosity and fractures of micrometer size as a consequence of corrosion, as well as a presence of phases mainly composed by tetra hydrated iron and manganese sulphates. The decreasing evolution of α vs t show the activity-passivity behavior in the corrosion process. Research article of journal indexed in ISI database Instituto Politecnico Nacional
URI :	http://www.repositoriodigital.ipn.mx/handle/123456789/10834
Otros identificadores :	1155-4339 http://hdl.handle.net/123456789/342
Aparece en las colecciones:	Doctorado

Ficheros en este ítem:

Fichero	Descripción	Tamaño	Formato
2005 JP IV v125 p217.pdf		163.68 kB	Adobe PDF	Visualizar/Abrir

El Instituto Politécnico Nacional