El Instituto Politécnico Nacional
Contribuye al desarrollo económico y social de la nación, a través de la formación integral de personas competentes; de la investigación, el desarrollo tecnológico y la innovación. Además tiene reconocimiento internacional por su calidad e impacto social.
Por favor, use este identificador para citar o enlazar este ítem:
http://repositoriodigital.ipn.mx/handle/123456789/10683Registro completo de metadatos
| Campo DC | Valor | Lengua/Idioma |
|---|---|---|
| dc.creator | Valverde Aguilar, Guadalupe | - |
| dc.creator | García Macedo, Jorge | - |
| dc.creator | Rentería Tapia, Victor | - |
| dc.creator | Aguilar Franco, Manuel | - |
| dc.date | 2012-03-16T19:49:44Z | - |
| dc.date | 2012-03-16T19:49:44Z | - |
| dc.date | 2011 | - |
| dc.date.accessioned | 2013-01-16T09:03:42Z | - |
| dc.date.available | 2013-01-16T09:03:42Z | - |
| dc.date.issued | 2013-01-16 | - |
| dc.identifier | http://hdl.handle.net/123456789/165 | - |
| dc.identifier.uri | http://www.repositoriodigital.ipn.mx/handle/123456789/10683 | - |
| dc.description | Gold metallic nanoparticles embedded in amorphous and crystalline TiO2 matrix as powders and films were synthesized by the sol–gel process at room temperature. The TiO2 matrix was synthesized by using tetrabutyl orthotitanate as the inorganic precursor. The films were spin-coated on glass wafers. The samples were annealed at at 100±C for 30 minutes and sintered at 520±C for 1 hour to generated anatase and rutile phases. The film shows a light blue colour. The amorphous film exhibits an absorption band at 568 nm. The crystalline film exhibit two absorption peaks located at around 402 (from TiO2 matrix) and 651 nm is due to the surface plasmon resonance of the gold nanoparticles. The films were studied using X-ray diffraction, infrared spectroscopy, scanning electron microscopy, high resolution transmission electronic microscopy and UV-Vis absorption spectroscopy. Photoconductivity studies were performed on amorphous and crystalline TiO2/Au films. The experimental data were fitted with straight lines at darkness and under illumination at 515 nm and 645 nm. This indicates an ohmic behavior. Transport parameters were calculated. | - |
| dc.language | en | - |
| dc.publisher | Revista Mexicana de Física | - |
| dc.subject | Gold nanoparticles | - |
| dc.subject | Titania | - |
| dc.title | Photoconductivity studies of gold nanoparticles supported on amorphous and crystalline TiO2 matrix prepared by sol-gel method | - |
| dc.type | Article | - |
| Aparece en las colecciones: | Doctorado | |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 57_2_0013 Photoconductivity TiO2_Au.pdf | 662.56 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.