Synthesis and Thermal Behavior of Metallic Cobalt Micro and Nanostructures

Por favor, use este identificador para citar o enlazar este ítem: http://repositoriodigital.ipn.mx/handle/123456789/10783

Título :	Synthesis and Thermal Behavior of Metallic Cobalt Micro and Nanostructures
Palabras clave :	Metallic Cobalt Cobalt nanoparticles; Magnetic nanoparticles; Hollow magnetic microparticles
Fecha de publicación :	16-ene-2013
Editorial :	NANO-MICRO LETTERS
Descripción :	In this contribution, a comparative study of metallic cobalt micro and nanoparticles obtained in solution by four different chemical routes is reported. Classic routes such as borohydride reduction in aqueous media and the so-called polyol methodology were used to obtain the cobalt nanostructures to be studied. Using CTAB as surfactant, cobalt hollow nanostructures were obtained. The use of strong reducing agents, like sodium borohydride, favors the formation of quasi-monodispersed nanoparticles of about 2 nm size but accompanied with impurities; for hydrazine (a mild reducer), nanoparticles of larger size are obtained which organize in spherical microagglomerates. Valuable information on the particles thermal stability and on nature of the species anchored at their surface was obtained from thermogravimetric curves. The samples to be studied were characterized from UV-vis, IR, X-ray diffraction, and electron microscopy images (scanning and transmission).
URI :	http://www.repositoriodigital.ipn.mx/handle/123456789/10783
Otros identificadores :	Nano-Micro Lett. 3 (1), 12-19 (2011). http://hdl.handle.net/123456789/288
Aparece en las colecciones:	Doctorado

Ficheros en este ítem:

Fichero	Descripción	Tamaño	Formato
Synthesis and Thermal Behavior of Metallic.pdf		145.53 kB	Adobe PDF	Visualizar/Abrir

El Instituto Politécnico Nacional