Título : | Synthesis and characterization of hafnium oxide films for thermo and photoluminescence applications |
Palabras clave : | Hafnium oxide films spray pyrolysis UV radiation dosimetry |
Fecha de publicación : | 16-ene-2013 |
Editorial : | ELSEVIER |
Descripción : | Hafnium oxide (HfO2) films were deposited by the ultrasonic spray pyrolysis process. The films were
synthesized from hafnium chloride as raw material in deionized water as solvent and were deposited on
corning glass substrates at temperatures from 300 to 600 1C. For substrate temperatures lower than
400 1C the deposited films were amorphous, while for substrate temperatures higher than 450 1C, the
monoclinic phase of HfO2 appeared. Scanning electron microscopy showed that the film’s surface
resulted rough with semi-spherical promontories. The films showed a chemical composition close to
HfO2, with an Hf/O ratio of about 0.5. UV radiation was used in order to achieve the thermoluminescent
characterization of the films; the 240nm wavelength induced the best response. In addition,
preliminary photoluminescence spectra, as a function of the deposition temperatures, are shown. Investigación INSTITUTO POLITECNICO NACIONAL |
URI : | http://www.repositoriodigital.ipn.mx/handle/123456789/11022 |
Otros identificadores : | Applied Radiation and Isotopes 68 (2010) 696-699 0969-8043 http://hdl.handle.net/123456789/534 |
Aparece en las colecciones: | Doctorado |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
2010-2 1.pdf | 61.7 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.