Por favor, use este identificador para citar o enlazar este ítem:
http://repositoriodigital.ipn.mx/handle/123456789/11613
Registro completo de metadatos
Campo DC | Valor | Lengua/Idioma |
---|---|---|
dc.creator | GUZMAN MENDOZA, JOSE | - |
dc.date | 2012-03-29T16:29:08Z | - |
dc.date | 2012-03-29T16:29:08Z | - |
dc.date | 2008 | - |
dc.date.accessioned | 2013-01-16T16:23:14Z | - |
dc.date.available | 2013-01-16T16:23:14Z | - |
dc.date.issued | 2013-01-16 | - |
dc.identifier | http://hdl.handle.net/123456789/1145 | - |
dc.identifier.uri | http://www.repositoriodigital.ipn.mx/handle/123456789/11613 | - |
dc.description | Trivalent samarium (Sm3+) doped hafnium oxide (HfO2) films were deposited using the spray pyrolysis deposition technique. The films were deposited on Corning glass substrates at temperatures ranging from 300 to 550 ◦C using chlorides as raw materials. Films, mostly amorphous, were obtained when deposition temperatures were below 350 ◦C. However, for temperatures higher than 400 ◦C, the films became polycrystalline, presenting the HfO2 monoclinic phase. Scanning electron microscopy of the films revealed a rough surface morphology with spherical particles. Also, electron energy dispersive analysis was performed on these films. The photoluminescence and cathodoluminescence characteristics of the HfO2 : SmCl3 films, measured at room temperature, exhibited four main bands centred at 570, 610, 652 and 716 nm, which are due to the well-known intra-4f transitions of the Sm3+ ion. It was found that the overall emission intensity rose as the deposition temperature was increased. Furthermore, a concentration quenching of the luminescence intensity was also observed. | - |
dc.language | en_US | - |
dc.publisher | IOP PUBLISHING | - |
dc.subject | HAFNIUM OXIDE | - |
dc.subject | SAMARIUM | - |
dc.title | Characterization of luminescent samarium doped HfO2 coatings synthesized by spray pyrolysis technique | - |
dc.type | Article | - |
Aparece en las colecciones: | Doctorado |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
RESUMEN HfO2.docx | 12.87 kB | Microsoft Word XML | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.