Título : | Characterization of luminescent samarium doped HfO2 coatings synthesized by spray pyrolysis technique |
Palabras clave : | HAFNIUM OXIDE SAMARIUM |
Fecha de publicación : | 16-ene-2013 |
Editorial : | IOP PUBLISHING |
Descripción : | Trivalent samarium (Sm3+) doped hafnium oxide (HfO2) films were deposited using the spray pyrolysis deposition technique. The films were deposited on Corning glass substrates at temperatures ranging from 300 to 550 ◦C using chlorides as raw materials. Films, mostly amorphous, were obtained when deposition temperatures were below 350 ◦C. However, for temperatures higher than 400 ◦C, the films became polycrystalline, presenting the HfO2 monoclinic phase. Scanning electron microscopy of the films revealed a rough surface morphology with spherical particles. Also, electron energy dispersive analysis was performed on these films. The photoluminescence and cathodoluminescence characteristics of the HfO2 : SmCl3 films, measured at room temperature, exhibited four main bands centred at 570, 610, 652 and 716 nm, which are due to the well-known intra-4f transitions of the Sm3+ ion. It was found that the overall emission intensity rose as the deposition temperature was increased. Furthermore, a concentration quenching of the luminescence intensity was also observed. |
URI : | http://www.repositoriodigital.ipn.mx/handle/123456789/11613 |
Otros identificadores : | http://hdl.handle.net/123456789/1145 |
Aparece en las colecciones: | Doctorado |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
RESUMEN HfO2.docx | 12.87 kB | Microsoft Word XML | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.